TÍNH CHẤT CƠ LÝ HÓA CỦA THÉP P8

Mác thép

C (%)

Si (%) (2)

Mn (%)

P (%) ≤

S (%) ≤

Cr (%)  ≤

Ni (%) ≤

Cu (%) ≤

Khử Oxy (1)

* TRUNG QUỐC TIÊU CHUẨN GB (GB 700-88)

Q195

0.06 ~ 0.12

≤ 0.30

0.25 ~ 0.5

0.045

0.050

0.30

0.30

0.30

F,b,Z

Q215A

0.009 ~ 0.15

≤ 0.30

0.25 ~ 0.5

0.045

0.050

0.30

0.30

0.30

F,b,Z

Q215B

0.009 ~ 0.15

≤ 0.30

0.25 ~ 0.5

0.045

0.050

0.30

0.30

0.30

F,b,Z

Q235A(3)

0.14 ~ 0.22

≤ 0.30

0.30 ~ 0.65(3)

0.045

0.050

0.30

0.30

0.30

F,b,Z

Q235B

0.12 ~ 0.20

≤ 0.30

0.30 ~ 0.70(3)

0.045

0.050

0.30

0.30

0.30

F,b,Z

Q235C

≤ 0.18

≤ 0.30

0.35 ~ 0.80

0.040

0.040

0.30

0.30

0.30

Z

Q235D

≤ 0.17

≤ 0.30

0.35 ~ 0.80

0.035

0.035

0.30

0.30

0.30

TZ

Q255A

0.18 ~ 0.28

≤ 0.30

0.40 ~ 0.70

0.045

0.045

0.30

0.30

0.30

Z

Q255D

0.18 ~ 0.28

≤ 0.30

0.40 ~ 0.70(1)

0.045

0.045

0.30

0.30

0.30

Z

Q275

0.28 ~ 0.38

≤ 0.35

0.50 ~ 0.80

0.045

0.050

0.30

0.30

0.30

Z

(1) F. Thép Sôi; b, thép nửa sôi; Z. thép lắng.

TZ thép lắng đặc biệt.

(2) Hàm lượng Si của thép kết cấu cacbon; F ≤ w Si 0.007%; Giới hạn dưới Si của Z là 0.012%

(3) Giới hạn trên w Mn của thép sôi Q345A và B là 0.60%.